The stirring cyanidation method is to concentrate and dewater the ore after the grinding and classification to a suitable concentration, and then add the cyanide solution, stir, inflate and leaching. The pulp in the leaching process or after the leaching is adsorbed by the activated carbon or the resin to absorb the dissolved gold , or the gold-containing solution after the solid-liquid separation is replaced with zinc to recover the gold. After the cyanide tailings are disinfected, they are sent to the tailings storage and storage.
When the gold ore contains a large amount of clay minerals, and the secondary slime is easily generated in the grinding, and the particulate gold content is high, the whole mud stirring cyanidation method can be used for gold extraction.
The stirring cyanidation method can be divided into two types: continuous and intermittent stirring cyanidation according to the leaching method.
When the gold is extracted by the continuous stirring cyanidation method, the slurry flows through several stirring barrels in series, and the slurry flows between the tanks by self-flow or pumping. When the cyanidation method is used for the gold extraction by intermittent stirring, the slurry is charged into several stirring leaching tanks which are operated in parallel, the gold leaching process is finished, and the slurry is discharged into the storage tank for filtration. Thereafter, another batch of new slurry is placed in the tank to continue leaching.
The continuous stirring cyanidation method has the following advantages over the batch method:
1) The production capacity of the leaching tank is improved because the loading and unloading time is saved;
2) No storage tanks, reducing infrastructure and production costs;
3) Automate the production process.
Aluminum alloy materials are widely used in all walks of life due to their low density, high strength and stiffness, good corrosion resistance, and good processing performance. At present, the proportion of aluminum alloy forging in the aluminum alloy industry is still relatively small. Due to the relatively high cost of aluminum alloy forging, the production technology is relatively difficult, and most of them are used in parts that are particularly important in stress. However, with the rapid development of the aerospace and automotive industries, the demand for aluminum alloy forgings is increasing day by day. In particular, the forgings on the aircraft account for a large proportion, mainly aluminum alloy forgings, because the aircraft has relatively high requirements for strength and weight. There is also an increasing demand for aluminum forgings in the automotive industry. Therefore, our future task is how to improve and improve the aluminum alloy forging technology to meet the increasing demands of the aluminum forging industry.
Aluminum alloy forging is relatively easy in the forging industry, and SCZY can easily deal with steel forgings, so under the condition of reasonable product structure, we can fully handle the production and service of aluminum forgings.
Aluminum Forging Parts,Forged Aluminum Parts,Aluminum Alloy Forgings,Aluminium Forging Automobile Parts,Aluminum Forgings,Aluminum Alloy Forging, Aluminium Forging, Aluminum Forging
Shenzhen SCZY Technology Co.,Ltd , https://www.szcasting.com